Investigation of failure analysis on fatigue crack initiation influenced by critical resolved shear stress in X10CrMoVNb9-1 steel

Investigation of failure analysis on fatigue crack initiation influenced by critical resolved shear stress in X10CrMoVNb9-1 steel

This study investigates the influences of the critical resolved shear stress (CRSS) values on calculating the number of cycles for the fatigue crack initiation cycle of X10CrMoVNb9-1 (P91) under cyclic loading conditions at room temperature while considering varied surface roughness on microstructur...

وصف كامل

التفاصيل البيبلوغرافية
الحاوية / القاعدة:ENGINEERING FAILURE ANALYSIS
المؤلفون الرئيسيون: Abd Rahim, Mohammad Ridzwan; Schmauder, Siegfried; Manurung, Yupiter H. P.; Bozic, Zeljko; Csanadi, Tamas; Binkele, Peter; Dusza, Jan; Verestek, Wolfgang; Ahmad, Meor Iqram Meor; Mat, Muhd. Faiz; Dogahe, Kiarash Jamali
التنسيق: مقال
اللغة:English
منشور في: PERGAMON-ELSEVIER SCIENCE LTD 2024
الموضوعات:
Engineering; Materials Science
الوصول للمادة أونلاين:https://www-webofscience-com.uitm.idm.oclc.org/wos/woscc/full-record/WOS:001403117600001

الانترنت

https://www-webofscience-com.uitm.idm.oclc.org/wos/woscc/full-record/WOS:001403117600001

مواد مشابهة