Wear mechanism of TiCN and TiALN coated drill in drilling of carbon steel
TiCN and TiAlN coated twist drills were subjected to drilling tests to investigate the failure mechanisms during drilling operation. The drilling tests were performed on a carbon steel plate with a thickness of 25 mm and the depth of drill was set at 20 mm. The drill performance parameters were set...
| الحاوية / القاعدة: | Jurnal Teknologi |
|---|---|
| المؤلف الرئيسي: | |
| التنسيق: | مقال |
| اللغة: | English |
| منشور في: |
Penerbit UTM Press
2015
|
| الوصول للمادة أونلاين: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-84943328611&doi=10.11113%2fjt.v76.5638&partnerID=40&md5=382c11def7e076cfb3630aa0fa252d52 |
| id |
Talib R.J.; Firdaus S.M.; Ismail N.I.; Hisyam Basri M.; Ariff H.M. |
|---|---|
| spelling |
Talib R.J.; Firdaus S.M.; Ismail N.I.; Hisyam Basri M.; Ariff H.M. 2-s2.0-84943328611 Wear mechanism of TiCN and TiALN coated drill in drilling of carbon steel 2015 Jurnal Teknologi 76 9 10.11113/jt.v76.5638 https://www.scopus.com/inward/record.uri?eid=2-s2.0-84943328611&doi=10.11113%2fjt.v76.5638&partnerID=40&md5=382c11def7e076cfb3630aa0fa252d52 TiCN and TiAlN coated twist drills were subjected to drilling tests to investigate the failure mechanisms during drilling operation. The drilling tests were performed on a carbon steel plate with a thickness of 25 mm and the depth of drill was set at 20 mm. The drill performance parameters were set at a spindle rotation of 1,600 rpm and feed rate of 20 mm/min. Each sample was then subjected to Scanning Electron Microscopy examination to investigate the wear mechanisms operated during drilling. Microstructural examination showed that the abrasion, adhesion and thermal wear mechanisms are operated during drilling process. © 2015 Penerbit UTM Press. All rights reserved. Penerbit UTM Press 1279696 English Article All Open Access; Bronze Open Access |
| author |
2-s2.0-84943328611 |
| spellingShingle |
2-s2.0-84943328611 Wear mechanism of TiCN and TiALN coated drill in drilling of carbon steel |
| author_facet |
2-s2.0-84943328611 |
| author_sort |
2-s2.0-84943328611 |
| title |
Wear mechanism of TiCN and TiALN coated drill in drilling of carbon steel |
| title_short |
Wear mechanism of TiCN and TiALN coated drill in drilling of carbon steel |
| title_full |
Wear mechanism of TiCN and TiALN coated drill in drilling of carbon steel |
| title_fullStr |
Wear mechanism of TiCN and TiALN coated drill in drilling of carbon steel |
| title_full_unstemmed |
Wear mechanism of TiCN and TiALN coated drill in drilling of carbon steel |
| title_sort |
Wear mechanism of TiCN and TiALN coated drill in drilling of carbon steel |
| publishDate |
2015 |
| container_title |
Jurnal Teknologi |
| container_volume |
76 |
| container_issue |
9 |
| doi_str_mv |
10.11113/jt.v76.5638 |
| url |
https://www.scopus.com/inward/record.uri?eid=2-s2.0-84943328611&doi=10.11113%2fjt.v76.5638&partnerID=40&md5=382c11def7e076cfb3630aa0fa252d52 |
| description |
TiCN and TiAlN coated twist drills were subjected to drilling tests to investigate the failure mechanisms during drilling operation. The drilling tests were performed on a carbon steel plate with a thickness of 25 mm and the depth of drill was set at 20 mm. The drill performance parameters were set at a spindle rotation of 1,600 rpm and feed rate of 20 mm/min. Each sample was then subjected to Scanning Electron Microscopy examination to investigate the wear mechanisms operated during drilling. Microstructural examination showed that the abrasion, adhesion and thermal wear mechanisms are operated during drilling process. © 2015 Penerbit UTM Press. All rights reserved. |
| publisher |
Penerbit UTM Press |
| issn |
1279696 |
| language |
English |
| format |
Article |
| accesstype |
All Open Access; Bronze Open Access |
| record_format |
scopus |
| collection |
Scopus |
| _version_ |
1828987882382032896 |