| Summary: | The goal of the present study was to determine the minimum thickness of monolithic zirconia required to achieve an acceptable masking ability and to examine how brand, thickness, and abutment substrate influenced that masking ability (ΔE). Seventy-two A2-shade monolithic zirconia disc specimens in various thicknesses (1.0, 1.5, and 2.0 mm) were fabricated using three brands: Nacera® Pearl 1, DD cubeX2 and XTCERA TT. A spectrophotometer was used to determine the CIELab values of the specimens, which were placed on a D4-shade resin composite and white acrylic (control) substrates. The ΔE was calculated and compared with the acceptable (AT = 5.5) and perceptible (PT = 2.6) tolerance thresholds. Further investigation was conducted on 72-disc specimens from the monolithic zirconia brand with the best masking ability on D3-shade resin composite and semi-precious alloy. Using two-way ANOVA, the interaction of thickness, brand, and abutment substrate on ΔE was investigated. Nacera® Pearl 1 at 1.5 mm thickness was sufficient to achieve AT on a D4-shade resin composite substrate, whereas 2.0 mm of DD cubeX2 and XTCERA TT were required. Nacera® Pearl 1 further testing on two other substrates requires thicknesses of 1.5 mm and 1.0 mm, respectively. Only the Nacera® Pearl 1 group achieved PT on D3- and D4-shade resin composite (2.0 mm) and semi-precious alloy substrates (1.5 mm). Brand, thickness, and abutment substrate influenced the ΔE (p < 0.001). To achieve an acceptable masking ability, the minimum thickness of monolithic zirconia tested on D3- and D4-shade resin composite and semi-precious alloy should be around 1.5 mm to 2.0 mm. © Penerbit Universiti Sains Malaysia. 2024
|
|---|