| Summary: | Here, we report the successful incorporation of group I elements (K, Na, Li) to ZnO nanowires. Three distinct (2, 4, and 6 wt.%) doping concentrations of group I elements have been used to generate high piezoelectric voltage by employing a vertically integrated nanowire generator (VING) structure. X-ray photoelectron spectra (XPS) indicated the seepage of dopants in ZnO nanowires by substitution of Zn. Shallow acceptor levels (LiZn, NaZn, KZn) worked as electron trapping centers for intrinsically n-type ZnO nanowires. Free moving electrons caused a leakage current through the nanowires and depleted their piezoelectric potential. Reverse leakage current is a negative factor for piezoelectric nanogenerators. A reduction in reverse leakage current signifies the rise in output voltage. A gradual rise in output voltage has been witnessed which was in accordance with various doping concentrations. K-doped ZnO nanowires have generated voltages of 0.85 V, 1.48 V, and 1.95 V. For Na-doped ZnO nanowires, the voltages were 1.23 V, 1.73 V, and 2.34 V and the voltages yeilded for Li-doped ZnO nanowires were 1.87 V, 2.63 V, and 3.54 V, respectively. Maximum voltage range has been further enhanced by the surface enrichment (oxidized with O2 molecules) of ZnO nanowires. Technique has been opted to mitigate the screening effect during an external stress. After 5 h of oxidation in a sealed chamber at 100 ppm, maximum voltage peaks were pronounced to 2.48 V, 3.19 V, and 4.57 V for K, Na, and Li, respectively. A low-cost, high performance mechanical transducer is proposed for self-powered devices. © 2022 by the authors.
|
|---|