AC Susceptibility and Electrical Properties of PbS added Bi1.6Pb0.4Sr2CaCu2O8 Superconductor; [Kerentanan Arus Ulang Alik dan Sifat Elektrik Superkonduktor Bi1.6Pb0.4Sr2CaCu2O8 dengan Penambahan PbS]

• Published in: Sains Malaysiana
• Main Author: Masnita M.J.; Awang R.; Abd-Shukor R.
• Format: Article
• Language: English
• Published: Penerbit Universiti Kebangsaan Malaysia 2022
• Online Access: https://www.scopus.com/inward/record.uri?eid=2-s2.0-85124649875&doi=10.17576%2fjsm-2022-5101-26&partnerID=40&md5=b0cd7f3c2863606128bccd9b20c275e0

The Bi1.6Pb0.4Sr2CaCu2O8 (Bi-2212) phase is an interesting superconductor. Although it's transition temperature is lower than Bi1.6Pb0.4Sr2Ca2Cu3O10 (Bi-2223), it has a better high field performance at low temperatures. This report is regarding the effects of lead sulfide on Bi1.6Pb0.4Sr2CaCu2O8 superconductor. Samples of Bi1.6Pb0.4Sr2CaCu2O8(PbS) x for x = 0.0 to 10.0 wt.% were prepared via the solid-state-reaction route. The Bi-2212 was the majority phase in all samples with x ≤ 1.0 wt.% showing more than 95%. Scanning electron micrographs showed increase in grain size as PbS content was increased. The x = 0 sample exhibited the highest Tc-zero at 72 K and Tc-onset 83 K. The imaginary part of the AC susceptibility showed that the peak temperature, Tp increased from 59 K for x = 0 to 66 K for x = 0.6 wt.% sample. This research showed that PbS increased the flux pinning of Bi-2212 for x ≤ 1.0 wt.% although the transition temperature was suppressed. © 2022 Penerbit Universiti Kebangsaan Malaysia. All rights reserved.