Averrhoa bilimbi pectin-based edible films: Effects of the linearity and branching of the pectin on the physicochemical, mechanical, and barrier properties of the films

The potential of Averrhoa bilimbi pectin (ABP) as a source of biopolymer for edible film (EF) production was explored, and deep eutectic solvent (DES) (1% w/w) containing choline chloride–citric acid monohydrate at a molar ratio of 1:1 was used as the plasticizer. The EF-ABP3:1, which was produced f...

Full description

Bibliographic Details
Published in:International Journal of Biological Macromolecules
Main Author: Shafie M.H.; Yusof R.; Samsudin D.; Gan C.-Y.
Format: Article
Language:English
Published: Elsevier B.V. 2020
Online Access:https://www.scopus.com/inward/record.uri?eid=2-s2.0-85088021120&doi=10.1016%2fj.ijbiomac.2020.07.109&partnerID=40&md5=36f020d2d29d729f51b50d08950fcc8c
Description
Summary:The potential of Averrhoa bilimbi pectin (ABP) as a source of biopolymer for edible film (EF) production was explored, and deep eutectic solvent (DES) (1% w/w) containing choline chloride–citric acid monohydrate at a molar ratio of 1:1 was used as the plasticizer. The EF-ABP3:1, which was produced from ABP with large branch size, showed a higher value of melting temperature (175.30 °C), tensile stress (7.32 MPa) and modulus (33.64 MPa). The EF-ABP3:1 also showed better barrier properties by obtaining the lowest water vapor transmission rates (1.10–1.18 mg/m2.s) and moisture absorption values (2.61–32.13%) depending on the relative humidity compared to other EF-ABPs (1.39–1.83 mg/m2.s and 3.48–51.50%, respectively) that have linear structure with smaller branch size. From these results, it was suggested that the galacturonic acid content, molecular weight, degree of esterification and pectin structure of ABP significantly influenced the properties of EFs. The interaction of highly branched pectin chains was stronger than the linear chains, thus reduced the effect of plasticizer and produced a mechanically stronger EF with better barrier properties. Hence, it was suggested that these EFs could be used as alternative degradable packaging/coating materials. © 2020 Elsevier B.V.