| Summary: | The Si doped ZnO nanopowders for varistor have been prepared at different sintering temperature using solid state method. The Si doped ZnO have been sintered at different temperatures 850, 950 and 1050°C at air condition. The structural and densification of Si doped ZnO were determined using scanning electron microscopy (SEM), X-ray diffraction (XRD) analysis and digital density meter. It was found that the average grain size of Si doped ZnO varistor were 0.81, 1.05 and 2.10μm when sintered at 850, 950 and 1050°C, respectively. The density of Si doped ZnO were 3.999, 4.453 and 5.332 g/cm3 when the sintering temperature increased from 850, 950 and 1050°C, respectively. The density and average grain size of the Si-Doped ZnO is increased with increase of sintering temperature. The Si doped ZnO varistor at different sintering process are polycrystalline structure. It is revealed that the sintering temperature can influence the properties of Si doped ZnO ceramics which is suitable to be used in varistor application. © 2019 Author(s).
|
|---|