| Summary: | A new organic-inorganic hybrid nanocomposite Zn-Al-MCPA-layered double hydroxide (ZAM) was prepared by intercalation of 2-methyl-4-chlorophenoxyacetic acid (MCPA) into Zn-Al-layered double hydroxide (ZAL) at various concentration of MCPA ranging from 0.1 to 0.7 M. The pH of the synthesis was kept constant at 7.5. Well-ordered hybrid nanocomposite was obtained with 0.4 M MCPA with an expansion of basal spacing from 8.9 Å in the ZAL to 19.7 Å in the resulting nanocomposite. The FTIR spectra of the nanocomposite show resemblance peaks of the MCPA and Zn-Al-layered double hydroxide indicating the inclusion of MCPA into the layered double hydroxide. The average particle size of ZAL and ZAM in this study was 115 and 128 nm, respectively. Percentage loading of MCPA was found to be 45.0 % (w/w), calculated based on the percentage of carbon in the sample. The release of MCPA into various aqueous solution was found to be dependent to the anion in the aqueous solution in the order of phosphate > sulfate > chloride with the percentage release of 80, 44, and 8 %, respectively. This study shows that Zn-Al-layered double hydroxide can be used as a host carrier for herbicide, MCPA, with controlled release capability. © 2012 Springer Science+Business Media Dordrecht.
|
|---|