A study of fatigue life of kenaf fibre composites
Towards green material, fatigue life of unidirectional kenaf fibre reinforced epoxy composites was investigated made from the hand-layout technique. The composites were subjected to tension-tension fatigue loading at stress ratio of 0.5 and 5 Hz of frequency. Fibre content ratios were found to affec...
| Published in: | Advanced Materials Research |
|---|---|
| Main Author: | |
| Format: | Conference paper |
| Language: | English |
| Published: |
2012
|
| Online Access: | https://www.scopus.com/inward/record.uri?eid=2-s2.0-84869434140&doi=10.4028%2fwww.scientific.net%2fAMR.576.757&partnerID=40&md5=64faf4c413b8026da0bc9961e16c7b9a |
| id |
2-s2.0-84869434140 |
|---|---|
| spelling |
2-s2.0-84869434140 Abdullah A.H.; Alias S.K.; Abdan K.; Ali A. A study of fatigue life of kenaf fibre composites 2012 Advanced Materials Research 576 10.4028/www.scientific.net/AMR.576.757 https://www.scopus.com/inward/record.uri?eid=2-s2.0-84869434140&doi=10.4028%2fwww.scientific.net%2fAMR.576.757&partnerID=40&md5=64faf4c413b8026da0bc9961e16c7b9a Towards green material, fatigue life of unidirectional kenaf fibre reinforced epoxy composites was investigated made from the hand-layout technique. The composites were subjected to tension-tension fatigue loading at stress ratio of 0.5 and 5 Hz of frequency. Fibre content ratios were found to affect fatigue life on the low cycle fatigue regime strongly as illustrated with stress level versus cycles to failure. It is found that kenaf fibre reinforced epoxy composites with higher fibre content posses higher load carrying capacity and degradation rates. © (2012) Trans Tech Publications, Switzerland. 10226680 English Conference paper |
| author |
Abdullah A.H.; Alias S.K.; Abdan K.; Ali A. |
| spellingShingle |
Abdullah A.H.; Alias S.K.; Abdan K.; Ali A. A study of fatigue life of kenaf fibre composites |
| author_facet |
Abdullah A.H.; Alias S.K.; Abdan K.; Ali A. |
| author_sort |
Abdullah A.H.; Alias S.K.; Abdan K.; Ali A. |
| title |
A study of fatigue life of kenaf fibre composites |
| title_short |
A study of fatigue life of kenaf fibre composites |
| title_full |
A study of fatigue life of kenaf fibre composites |
| title_fullStr |
A study of fatigue life of kenaf fibre composites |
| title_full_unstemmed |
A study of fatigue life of kenaf fibre composites |
| title_sort |
A study of fatigue life of kenaf fibre composites |
| publishDate |
2012 |
| container_title |
Advanced Materials Research |
| container_volume |
576 |
| container_issue |
|
| doi_str_mv |
10.4028/www.scientific.net/AMR.576.757 |
| url |
https://www.scopus.com/inward/record.uri?eid=2-s2.0-84869434140&doi=10.4028%2fwww.scientific.net%2fAMR.576.757&partnerID=40&md5=64faf4c413b8026da0bc9961e16c7b9a |
| description |
Towards green material, fatigue life of unidirectional kenaf fibre reinforced epoxy composites was investigated made from the hand-layout technique. The composites were subjected to tension-tension fatigue loading at stress ratio of 0.5 and 5 Hz of frequency. Fibre content ratios were found to affect fatigue life on the low cycle fatigue regime strongly as illustrated with stress level versus cycles to failure. It is found that kenaf fibre reinforced epoxy composites with higher fibre content posses higher load carrying capacity and degradation rates. © (2012) Trans Tech Publications, Switzerland. |
| publisher |
|
| issn |
10226680 |
| language |
English |
| format |
Conference paper |
| accesstype |
|
| record_format |
scopus |
| collection |
Scopus |
| _version_ |
1809677688417288192 |